PA12-CF | 3dprintingservice | Online 3D Printing Prototype, Mass Production Instant Quote and Order Service



As a kind of 3D printing material, the anthracite black, carbon-fibre filled polyamide 12 material stands out for excellent stiffness and a maximised weight-strength-ratio. Laser-sintered parts made from Carbon Fiber Filled PA12 possess excellent material properties.

Key Benefits
Enhanced stiffness
High resistance to thermal deformation
Excellent strength and hardness
Light weight

Technical Specifications

Object model printed with PA12-CF material

Appearance Black
Printing Process Selective laser sintering
Maximum part dimensions 1000×500×450mm
Layer thickness 0.06~0.3mm adjustable
Laser Type 2 x CO2 100W
Scanning Speed 15.2 m/s
Max. Chamber Temperature 220°C
Tensile strength 65-70MPa
Tensile Modulus 4700-6500 MPa
Flexural Strength 94-113 MPa
Flexural Modulus 4700-6500MPa
Impact Strength 4.3 KJ/M
Heat deflection temperature (0.46 MPa) 168 °C