Best TITANIUM ALLOY Material | 3D Printing Service | Lava - China


Titanium Alloy

EOS Titanium Ti64 is a Ti6Al4V alloy.As a kind of 3D printing material, this well-known light alloy is characterized by having excellent mechanical properties and corrosion resistance combined with low specific weight. The ELI version (extra-low interstitials) has particularly high purity.

Key Benefits
Light weight with high specific strength (strength per density)
Corrosion resistance
commonly used in biomedical applications
Laser-sintered parts fulfil requirements of ASTM F1472 (for Ti6Al4V) and ASTM F136 (for Ti6Al4V ELI) regarding maximum concentration of impurities
Very good bioadhesion (cell growth tested with good results)

Technical Specifications

Object model printed with Titanium Alloy material

Appearance Grey
Printing Process Direct Metal Laser Sintering (DMLS)
Maximum part dimensions 400 x 400 x 400 mm (15.8 x 15.8 x 15.8 in)
Laser type Yb-fiber laser; 1 kW
Precision optics F-theta-lens
Scan speed up to 7.0 m/s (23 ft/s)
Focus diameter approx. 90 µm (0.0035 in)
Layer thickness 20μm
Volume rate 1.68mm3/s
Part density 4.4g/cm3
Surface roughness after shot-peening Approx.Ra 4μm
Part accuracy after shot-peening ±50μm
Min. wall thickness 0.3mm
Average defect amount 0.02%
Ultimate tensile strength(XY),Rm 1077Mpa
Ultimate tensile strength(Z),Rm 1065Mpa
Yield strength(XY),Rp0.2 964Mpa
Yield strength(Z),Rp0.2 956Mpa